A Study on the Mechanical Properties of Concrete by Replacing Sand with Waste Foundry Sand
1460399308-IJETAEtobecorrected.docx (Size: 190.81 KB / Downloads: 13)
Abstract-- Conservation of natural resources and preservation of environment is the essence of any development. The problem arising from continuous technological and industrial development is the disposal of waste material. If some of the materials are found suitable in concrete making not only cost of construction can be put down, but also safe disposal of waste materials can be achieved.
I. INTRODUCTION
Concrete is a composite material composed of gravels or crushed stones (coarse aggregate), sand (fine aggregate) and hydrated cement (binder). It has been in use for over a century in all construction works. A variety of new materials in the field of concrete technology have been developed during the recent past with the ongoing demand of construction industries to meet the functional, strength, economical and durability requirements.
rapid increase in disposal cost. In an effort to use the WFS in large volume, research has being carried out for its possible large scale utilization in making concrete as partial replacement of fine aggregate
Foundry industry produces a large amount of by-product material during casting process. The ferrous metal casts in foundry are cast iron and steel, non ferrous metal are aluminum, copper, brass and bronze. Over 70% of the total by-product material consists of sand because moulds consist usually of molding sand, which is easily available, inexpensive, resistance to heat damage and easily bonded with binder and other organic material in mould. Foundry industry use high quality specific size silica sand for their molding and casting process. These WFS is black in color and contain large amount of fines. The typical physical and chemical property of WFS is dependent upon the type of metal being poured, casting process, technology employed, type of furnaces (induction, electric arc and cupola) and type of finishing process (grinding, blast cleaning and coating).
II. LITERATURE REVIEW
Rafat Siddique et al. (2008) presented the results of an experimental investigation carried out to evaluate the mechanical properties of concrete mixtures in which fine aggregate (regular sand) was partially replaced with usedfoundry sand (UFS). Fine aggregate was replaced with three percentages (10%, 20%, and 30%) of UFS by weight. Tests were performed for the properties of fresh concrete.
83
Compressive strength, splitting- tensile strength, flexural strength, and modulus of elasticity were determined at 28, 56, 91, and 365 days. Test results indicated a marginal increase in the strength properties of plain concrete by the inclusion of UFS as partial replacement of fine aggregate (sand) and that can be effectively used in making good quality concrete and construction materials.
Gurpreet Singh and Rafat Siddique (2011) carried out an experimental investigation to evaluate the strength and durability properties of concrete mixtures, in which natural sand was partial replaced with (WFS). Natural sand was replaced with five percentage (0%, 5%, 10%, 15%, and 20%) of WFS by weight. Compression test and splitting tensile strength test were carried out to evaluate the strength properties of concrete at the age of 7, 28 and 91 days. Test results indicate a marginal increase in strength properties of plain concrete by inclusion of WFS as a partial replacement of fine aggregate.
H. Merve Basar and Nuran Deveci Aksoy (2012) studied the potential re-use of waste foundry sand (WFS) in readymixed concrete (RMC) production. Regular sand was replaced with five percentages (0%, 10%, 20%, 30%, 40%) of WFS by weight and solidification/stabilization (S/S) process was applied to all concrete mixtures. Three aspects were investigated for the qualification of WFS-based-RMC, i.e., the mechanical, leaching and micro-structural properties. Various tests for the mechanical and physical performance of the solidified products were carried out, and the results indicated that the addition of WFS as partial replacement of sand reduced the strength performance and density and also increased the water absorption ratio of the concrete mixtures. Nevertheless, the concrete having 20% WFS exhibited almost similar results with the control one. The findings of this research suggest that WFS can be effectively utilized in making good quality RMC as a partial replacement of fine aggregates with no adverse mechanical, environmental and micro-structural impacts; however, the partial replacement should not exceed 20%.
Rafat Siddique and El-Hadj Kadri (2011)dealt with the effect of foundry sand (FS) and metakaolin (MK) on the near surface characteristics of concrete. A control concrete having cement content 450 kg/m3 and w/c of 0.45 was designed. Cement was replaced with three percentages (5%, 10%, and 15%) of metakaolin weight, and fine aggregates were replaced with 20% foundry sand. Tests were conducted for initial surface absorption, sorptivity, water absorption and compressive strength at the ages of 35, 56, and 84 days.
III. EXPERIMENTAL INVESTIGATION
A. Materials
Cement: Ordinary Portland cement (Ultra tech cement) of 53 grade confirming to IS: 12269-1987was used. It was tested for its physical properties as per IS 4031 (part II)-1988 and chemical properties as per IS: 12269 at lucid laboratories, Hyderabad.
Aggregate: The size, shape and gradation of the aggregate play an important role in achieving a proper concrete. The flaky and elongated particles will lead to blocking problems in confined zones. The sizes of aggregates will depend upon the size of rebar spacing.
The coarse aggregate chosen for Concrete was typically angular in shape, well graded, and smaller than maximum size suited for conventional concrete; typical conventional concreteshould have a maximum aggregate size of 20mm. Gradation is an important factor in choosing a coarse aggregate. Gap-graded coarse aggregate promotes
segregation to a greater degree than the well graded coarse aggregate.
Fine Aggregate: The locally available river sand was used as fine aggregate in the present investigation. The sand was free from clayey matter, salt and organic impurities. The sand was tested for various properties like specific gravity, bulk density etc., and in accordance with IS 2386-1963.
Coarse Aggregate: Machine crushed angular granite metal of 20mm nominal size from the local source was used as coarse aggregate. It was free from impurities such as dust, clay particles and organic matter etc. The physical properties of coarse aggregate were investigated in accordance with IS 2386 -1963.
Waste Foundry Sand: Waste foundry sand was obtained locally from Hinduja Casting Uppal Hyderabad. WFS was used as a partial replacement of fine aggregate (natural river sand). Metal poured in the foundry is gray iron. The sand was tested for various properties like specific gravity, bulk density etc., and in accordance with IS 2386-1963. The fine aggregate was conforming to standard specifications.
Water: Locally available water used for mixing and curing which is potable and is free from injurious amounts of oils, acids, alkalis, salts, sugar, organic materials or other substances that may be deleterious to concrete or steel.
Super Plasticizer: Super plasticizer conforming to IS9103-1979 by trade name Conplast SP 430 manufactured by Fosroc Chemicals (India) limited obtained from United Engineering, Rani Ganj, Hyderabad was used as a water reducing agent to achieve the required workability.
B. Mixes:
The present experiment is carried out to investigate strength properties of concrete mixes of grade M30 in which fine aggregate (river sand) is to be fully replaced with Waste Foundry Sand. Fine aggregate will be replaced with six percentages (10%, 20%, 30%, 40%, 50%
,60%,70%,80%,90%,100%) of WFS by weight.
C. Mixing, Casting, Curing and Testing:
All the triple blended composites were mixed in the pan mixer. Required number of specimens for various combinations were cast. Continuous curing was maintained upto the age of 7, 28 & 56 days. Mixing, casting, curing and testing were carried out as per the standard specifications.